0.12mm 80/20 Intambo ye-Nichrome Yezifudumezi Zezimboni
Ama-alloys e-Nickel Chrome (NiCr) yizinto ezimelana kakhulu nezivamile ezisetshenziswa ezinhlelweni zokusebenza ezinamazinga okushisa aphezulu afika ku-1,250°C (2,280°F).
Lawa ma-alloys e-Austenitic aziwa ngamandla awo okusebenza aphezulu emazingeni okushisa uma kuqhathaniswa nama-alloys e-FeCrAl kanye namandla awo aphezulu okukhasa. Ama-alloys e-Nickel Chrome nawo ahlala e-ductile ngaphezulu uma eqhathaniswa nama-alloys e-FeCrAl ngemva kwesikhathi eside ezingeni lokushisa. I-Chromium Oxide emnyama (Cr2O3) yakheka kumazinga okushisa aphakeme angenwa kalula ama-spalling, noma ukubhakuzisa, okubangela ukungcola okungaba khona kuye ngohlelo lokusebenza. Le oxide ayinazo izinto zokuvala ugesi njenge-Aluminium Oxide (Al2O3) yama-alloys e-FeCrA. Ama-alloys e-Nickel Chrome abonisa ukumelana nokugqwala okuhle ngaphandle kwezindawo lapho kukhona khona isulfure.
| Ibanga | I-Ni80Cr20 | I-Ni70Cr30 | I-Ni60Cr23 | I-Ni60Cr15 | I-Ni35Cr20 | I-Karma | Evanohm | |
| Ukuqamba amagama% | Ni | U-Bal | U-Bal | 58.0-63.0 | 55.0-61.0 | 34.0-37.0 | U-Bal | U-Bal |
| Cr | 20.0-23.0 | 28.0-31.0 | 21.0-25.0 | 15.0-18.0 | 18.0-21.0 | 19.0-21.5 | 19.0-21.5 | |
| Fe | ≦1.0 | ≦1.0 | U-Bal | U-Bal | U-Bal | 2.0-3.0 | - | |
| I-Al1.0-1.7 Ti 0.3-0.5 | Al2.7-3.2 Mn0.5-1.5 | Al2.7-3.2 Cu2.0-3.0 Mn0.5-1.5 | ||||||
| Izinga lokushisa eliphezulu (°C) | 1200 | 1250 | 1150 | 1150 | 1100 | 300 | 400 | |
| I-Resisivity(Ω/cmf,20℃) | 1.09 | 1.18 | 1.21 | 1.11 | 1.04 | 1.33 | 1.33 | |
| Ukungazweli (uΩ/m,60°F) | 655 | 704 | 727 | 668 | 626 | 800 | 800 | |
| Ukuminyana(g/cm³) | 8.4 | 8.1 | 8.4 | 8.2 | 7.9 | 8.1 | 8.1 | |
| I-Thermal Conductivity(KJ/m·h·℃) | 60.3 | 45.2 | 45.2 | 45.2 | 43.8 | 46.0 | 46.0 | |
| I-Linear Expansion Coefficient(×10¯6/℃)20-1000℃) | 18.0 | 17.0 | 17.0 | 17.0 | 19.0 | - | - | |
| I-Melting Point(℃) | 1400 | 1380 | 1370 | 1390 | 1390 | 1400 | 1400 | |
| Ukuqina(Hv) | 180 | 185 | 185 | 180 | 180 | 180 | 180 | |
| Amandla Okuqina(N/mm2 ) | 750 | 875 | 800 | 750 | 750 | 780 | 780 | |
| Ubude(%) | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | 10-20 | 10-20 | |
| Isakhiwo seMicrographic | i-austenite | i-austenite | i-austenite | i-austenite | i-austenite | i-austenite | i-austenite | |
| I-MagneticProperty | Cha | Cha | Cha | Kancane | Cha | Cha | Cha | |
| Impilo Esheshayo(h/℃) | ≥81/1200 | ≥50/1250 | ≥81/1200 | ≥81/1200 | ≥81/1200 | - | - | |