I-0Cr25Al5 ingxubevange ye-iron-chromium-aluminium (i-FeCrAl alloy) ibonakala ngokumelana okuphezulu, i-coefficient ephansi yokumelana nogesi, izinga lokushisa eliphezulu lokusebenza, ukumelana nokugqwala okuhle ngaphansi kwezinga lokushisa eliphezulu.Ifanele ukusetshenziswa emazingeni okushisa afika ku-1250 ° C.
Izinhlelo zokusebenza ezijwayelekile ze-0Cr25Al5 zisetshenziswa endaweni yokupheka ye-ceramic kagesi, isithando somlilo sezimboni, izifudumezi.
Ukwakheka okujwayelekile%
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Okunye |
Ubukhulu | |||||||||
0.06 | 0.025 | 0.025 | 0.70 | Ubukhulu 0.60 | 23.0~26.0 | Ubukhulu 0.60 | 4.5~6.5 | U-Bal. | - |
Izakhiwo ezijwayelekile zikaMechanical(1.0mm)
Amandla esivuno | Amandla Okuqina | Ukwelula |
Mpa | Mpa | % |
500 | 700 | 23 |
Izakhiwo ezibonakalayo ezijwayelekile
Ukuminyana (g/cm3) | 7.10 |
Ukumelana nogesi ku-20ºC(ohm mm2/m) | 1.42 |
I-coefficient ye-Conductivity ku-20ºC (WmK) | 13 |
I-coefficient yokwanda kwe-thermal
Izinga lokushisa | I-Coefficient of Thermal Expansion x10-6/ºC |
20 ºC-1000ºC | 15 |
Umthamo wokushisa othize
Izinga lokushisa | 20ºC |
J/gK | 0.46 |
Iphoyinti lokuncibilika (ºC) | 1500 |
Izinga lokushisa eliphezulu eliqhubekayo lokusebenza emoyeni (ºC) | 1250 |
Izakhiwo kazibuthe | kazibuthe |