I-China 1.2mm 1.6mm 2.4mm 3.17mm I-Aluminium MIG TIG Welding Wire Rod Er4043 Er4047 Er5356 Er5183 Ukukhiqiza kanye Nemboni

1.2mm 1.6mm 2.4mm 3.17mm Aluminium MIG TIG Welding Wire Rod Er4043 Er4047 Er5356 Er5183

Incazelo emfushane:

1.2mm 1.6mm 2.4mm 3.17mm Aluminium MIG TIG Welding Wire Rod Er4043 Er4047 Er5356 Er5183

I-ER4043 5% okuqukethwe kwe-Si, i-aluminium silicon alloy welding wire, inoketshezi oluhle.
Isetshenziselwa i-welding forging and casting materials ngenxa yokuzwela okuphansi kokuqhekeka okushisayo.
Kulula ukukhiqiza i-brittle Mg2Si emthungoni wokushisela ngesikhathi sokushisela, okunciphisa ipulasitiki nokumelana nokugqwala kwelunga.
I-welding inhle futhi ikhanya, i-arc izinzile, i-spatter incane, kodwa ngemva kwe-anodizing, umbala uhlukile kusisekelo sensimbi.

Ubude Obunwetshiwe:10-20 mm

Iphakheji:0.5kg/1kg/5kg/7kg

Ukucaciswa:0.8~3.2mm

Ikhodi ye-HS:8311300000

Amandla Okukhiqiza:150ton/ngenyanga

Amandla Okugcina:462MPa

Thumela i-imeyili kithi

Imininingwane Yomkhiqizo

FAQ

Omaka bomkhiqizo

Okujwayelekile: AWS A5.10 ER4043	Ukwakheka Kwekhemikhali %
	Si	Fe	Cu		Mn	Zn	Okunye				AL
Ibanga ER4043	4.5 - 6.0	≤ 0.80	≤ 0.30		≤ 0.05	≤ 0.10	-				Phumula
Uhlobo	I-Spool (MIG)					Ishubhu (TIG)
Ukucaciswa (MM)	0.8,0.9,1.0,1.2,1.6,2.0					1.6,2.0,2.4,3.2,4.0,5.0
Iphakheji	S100/0.5kg S200/2kg S270,S300/6kg-7kg S360/20kg					5kg / ibhokisi 10kg / ibhokisi ubude :1000MM
Izakhiwo Zemishini	Fusion Temperature ºC		Ezogesi I-IACS	Ukuminyana g/mm3		I-tensile Mpa		Veza Mpa		Ukwelula %
	575 - 630		42%	2.68		130 - 160		70 - 120		10-18
	Ububanzi(MM)		1.2			1.6			2.0
I-MIG Ukushisela	I-Welding Yamanje - A		180 - 300			200 - 400			240 - 450
	I-Welding Voltage - V		18-26			20-28			22-32
I-TIG Ukushisela	Ububanzi (MM)		1.6 - 2.4			2.4 - 4.0			4.0 - 5.0
	I-Welding Yamanje - A		150 - 250			200 - 320			220 - 400
Isicelo	Kunconyelwe ukushisela i-6061 ,6XXX uchungechunge;3XXXand2XXX uchungechunge lwe-aluminium alloy.
Qaphela	1, Umkhiqizo ungagcinwa iminyaka emibili ngaphansi kwesimo sokupakishwa kwefekthri futhi uvalwe, kanye ne ukupakisha kungasuswa izinyanga ezintathu ngaphansi kwemvelo evamile yomoya. 2,Imikhiqizo kufanele igcinwe endaweni engenawo umoya, eyomile nasendaweni. 3, Ngemuva kokuthi ucingo lususiwe ephaketheni, kunconywa ukuthi kube nesembozo esifanele sokuvikela uthuli zifakwe phezu kocingo.

Uchungechunge lwe-almunium alloy welding:

Into	AWS		I-Aluminium Alloy Chemical Composttion(%)
Into	AWS		Cu	Si	Fe	Mn	Mg	Cr	Zn	Ti	AL
I-Aluminium Ehlanzekile	ER1100		0.05-0.20	1.00		0.05			0.10		99.5
	ER1100		0.05-0.20	1.00		0.05			0.10		99.5	Ipulasitiki enhle, yokushisela igesi evikelayo noma i-argon arc welding ye-aluminium emsulwa engagqwali.
	Ingxube ye-aluminium	ER5183		0.10	0.40	0.40	0.50-1.0	4.30-5.20	0.05-0.25	0.25	0.15	Rem
Amandla aphezulu, ukumelana nokugqwala okuhle, okwe-argon arc welding.
ER5356			0.10	0.25	0.40	0.05-0.20	4.50-5.50	0.05-0.20	0.10	0.06-0.20	Rem
Amandla aphezulu, ukumelana nokugqwala okuhle, okwe-argon arc welding.
ER5087			0.05	0.25	0.40	0.70-1.10	4.50-5.20	0.05-0.25	0.25	0.15	Rem
Ukumelana nokugqwala okuhle, ukushisela kanye nepulasitiki, yokushisela igesi yokuvikela noma i-argon arc welding.
ER4047			0.30	11.0-13.0	0.80	0.15	0.10		0.20		Rem
Ikakhulukazi i-brazing kanye ne-soldering.
ER4043			0.30	4.50-6.00	0.80	0.05	0.05		0.10	0.20	Rem
Ukumelana nokugqwala okuhle, ukusetshenziswa okubanzi, isivikelo segesi noma i-argon acr welding.