  • I-Constantan Flat Wire Copper Nickel Alloy 6j40 Ribbon 0.4*2mm
  • I-Constantan Flat Wire Copper Nickel Alloy 6j40 Ribbon 0.4*2mm

I-Constantan Flat Wire Copper Nickel Alloy 6j40 Ribbon 0.4*2mm

Incazelo emfushane:

I-Constantan Flat Wire Copper Nickel Alloy 6j11 Ribbon 0.4*2mm

Ukungazweli ( 200C μ Ω . m): 0.1
Ubukhulu. Izinga lokushisa elisebenzayo (0C):200
Amandla Okuqina (Mpa):≥ 250
Iphuzu elincibilikayo (0C):1095
Ukuminyana ( g/cm3):8.9
I-TCR x10-6/ 0C (20~600 0C): < 100


  • Isitifiketi:ISO9001
  • Usayizi:Kwenziwe ngokwezifiso
  • igama lomkhiqizo:I-Copper Nickel Alloy 6j11
  • isicelo:imboni
  • impahla :ingxubevange
  • isici:ukumelana okuphezulu
  • umsebenzi:ukuzinza kwefomu elihle
  • isisindo:okusekelwe
  • ubukhulu:njengemfuneko yeklayenti
  • umbala:nsundu
  • umumo:ucingo
  • I-MOQ:20kg

    • Imininingwane Yomkhiqizo

    FAQ

    Omaka bomkhiqizo

    I-New Constantan Flat Wire Copper Nickel Alloy 6j11 Ribbon 0.4*2mm

    Isici Ukungazweli ( 200C μ Ω . m) Ubukhulu. Izinga lokushisa elisebenzayo (0C) Amandla Okuqina (Mpa) Iphoyinti lokuncibilika (0C) Ukuminyana (g/cm3) I-TCR x10-6/ 0C (20~600 0C) I-EMF vs Cu (μ V/ 0C) (0~100 0C)
    I-alloy Nomenclature
    I-NC003 (CuNi1) 0.1 200 ≥ 250 1095 8.9 < 100 -12

     

    Izakhiwo Zomzimba Imethrikhi Amazwana
    Ukuminyana 8.94 g/cc
    Izakhiwo Zemishini Imethrikhi Amazwana
    Amandla Aqinile, Okugcina 262 - 531 MPa
    Amandla Aqinile, Yield 276 - 524 MPa Kuya ngentukuthelo
    Elongation at Break 46.0 % kwe 50.8 mm.
    I-Modulus ye-Elasticity 115 GPA
    I-Poissons Isilinganiso 0.310 Kubaliwe
    Ukusebenziseka kalula 20 % I-UNS C36000 (ithusi elisika mahhala) = 100%
    Shear Modulus 44.0 GPA
    Izakhiwo zikagesi Imethrikhi Amazwana
    Ukungazweli Kagesi 0.0000120 ohm-cm
    @Izinga lokushisa 20.0 ° C
    Izakhiwo ezishisayo Imethrikhi Amazwana
    CTE, linear 17.5 µ m/m-° C
    @Izinga lokushisa 20.0 – 300 ° C
    Amandla Okushisa athize 0.380 J/g-° C
    I-Thermal Conductivity 64.0 W/mK
    @Izinga lokushisa 20.0 ° C
    I-Melting Point < = 1125 ° C I-Liquidus
    I-Liquidus 1125 ° C
    Icubungula izakhiwo Imethrikhi Amazwana
    I-Annealing Temperature 565 - 815 ° C
    I-Hot-Working Temperature 815 – 950 ° C
    Izakhi Zezakhi Imethrikhi Amazwana
    Copper, Ku > = 91.2 %
    Iron, Fe 1.30 - 1.70 %
    Umholi, Pb < = 0.050 %
    IManganese, Mn 0.30 - 0.80 %
    Nickel, Ni 4.80 - 6.20 %
    Zinc, Zn < = 1.0 %

    I-CuNi44 Chemical Content, %

    Ni Mn Fe Si Cu Okunye I-ROHS Directive
    Cd Pb Hg Cr
    44 1% 0.5 - U-Bal - ND ND ND ND

    Izakhiwo Zemishini

    I-Max Continuous Service Temp 400ºC
    I-resissive ku-20ºC 0.49±5%ohm mm2/m
    Ukuminyana 8.9 g/cm3
    I-Thermal Conductivity -6(Ubukhulu)
    I-Melting Point 1280ºC
    Amandla Okuqina,N/mm2 Okufakiwe,Athambile 340 ~ 535 Mpa
    Amandla Okuqina,N/mm3 Okubandayo Okugoqiwe 680 ~ 1070 Mpa
    Ubude (onyaka) 25%(Amaminithi)
    Ubude (okubandayo okugoqiwe) ≥Amaminithi)2%(Amaminithi)
    I-EMF vs Cu, μV/ºC (0~100ºC) -43
    Isakhiwo seMicrographic i-austenite
    Impahla Magnetic Cha

     