I-China Constantan Wire 6J40 wire yokushisisa Ukukhiqiza kanye Nemboni

Intambo ye-Constantan Wire 6J40 yokushisa

Incazelo emfushane:

I-Constantan Wire enokumelana okulinganiselwe kanye ne-coefficient yokushisa ephansi yokumelana ne-flat resistance/temperature curve ebanzi kune-"manganins". I-Constantan iphinde ibonise ukumelana nokugqwala okungcono kune-man ganins. Ukusetshenziswa kuvame ukukhawulelwa kumasekethe e-ac.
Intambo yaseConstantan nayo iyisici esingesihle se-thermocouple yohlobo lwe-J lapho i-Iron iyi-positive; ama-thermocouple ohlobo lwe-J asetshenziswa ekusetshenzisweni kokwelapha ukushisa. Futhi, iyisici esingesihle se-thermocouple yohlobo lwe-T ene-OFHC Copper eyi-positive; ama-thermocouple ohlobo lwe-T asetshenziswa emazingeni okushisa acwebezelayo.

Sithumelele i-imeyili

Imininingwane Yomkhiqizo

Imibuzo Evame Ukubuzwa

Amathegi Omkhiqizo

I-Constantan Eureca Wire / Flat Wire
Incazelo Yomkhiqizo
I-Constantan Wire enokumelana okulinganiselwe kanye ne-coefficient yokushisa ephansi yokumelana ne-flat resistance/temperature curve ebanzi kune-"manganins". I-Constantan iphinde ibonise ukumelana nokugqwala okungcono kune-man ganins. Ukusetshenziswa kuvame ukukhawulelwa kumasekethe e-ac.
Intambo yaseConstantan nayo iyisici esingesihle se-thermocouple yohlobo lwe-J lapho i-Iron iyi-positive; ama-thermocouple ohlobo lwe-J asetshenziswa ekusetshenzisweni kokwelapha ukushisa. Futhi, iyisici esingesihle se-thermocouple yohlobo lwe-T ene-OFHC Copper eyi-positive; ama-thermocouple ohlobo lwe-T asetshenziswa emazingeni okushisa acwebezelayo.

Okuqukethwe Kwamakhemikhali, %

Ni	Mn	Fe	Si	Cu	Okunye	Isiqondiso se-ROHS
						Cd	Pb	Hg	Cr
44	1.50%	0.5	-	I-Bal	-	ND	ND	ND	ND

Izakhiwo Zemishini

Izinga Lokushisa Eliphezulu Lesevisi Eqhubekayo	400ºC
Ukuqina kokushisa ku-20ºC	0.49±5%ohm mm2/m
Ubuningi	8.9 g/cm3
Ukuqhuba Okushisayo	-6 (Ubuningi)
Indawo Yokuncibilika	1280ºC
Amandla Okuqina, i-N/mm2 ehlanganisiwe, ethambile	340~535 Mpa
Amandla Okuqina, i-N/mm3 Cold Rolled	680~1070 Mpa
Ukwelulwa (i-anneal)	25% (Ubuncane)
Ukwelulwa (okugoqwe okubandayo)	≥Min)2% (Min)
I-EMF vs i-Cu, μV/ºC (0~100ºC)	-43
Isakhiwo se-Micrographic	i-austenite
Impahla Kamagnetic	Cha