I-Fecral 135 Alloy Electric Resistance Heating Wire 0cr25al5 0cr23al5 0cr21al6 Yamakhoyili Okushisa
I-FeCrAl 135 Alloy Electric Resistance Heating Wire Ocr25al5 Ocr23al5 Ocr21al6 yamakhoyili weHeater
I-FeCrAl135 iyingxubevange ye-ferritic iron-chromium-aluminium (FeCrAl alloy) ukuze isetshenziswe emazingeni okushisa afika ku-1300°C (2370°F).I-alloy ibonakala ngokumelana okuphezulu nokumelana okuhle kwe-oxidation.
I-FeCrAl135 isetshenziswa ezintweni zikagesi zasendlini nasezikolweni zezimboni.Izinto ezijwayelekile ezisetshenziswa ezinsizeni zasekhaya zihlanganisa izakhi zensimbi ezineshehethi zeshubhu zama-ayina, izakhi ezishumekwe ku-ceramic yezifudumezi zephaneli, izakhi ze-cartridge ezifayo zensimbi, izintambo zokufudumeza nezifudumezi zezintambo ezintweni ezincibilikisayo nezikhiphayo, izakhi ze-mica ezisetshenziswa kuma-ayina, izifudumezi zamashubhu e-quartz zokushisisa isikhala. , okomisi obona ngeso lefoni ezimbonini, kumakhoyili ku-ceramic fibre yamapuleti abilayo anamahob e-ceramic, kumakhoyili avale ubuhlalu ama-heater panel, kuma-elementi amakhoyili amisiwe wezifudumezi zomoya ezikomisini elondolo.
Ezinhlelweni zezimboni i-FeCrAl135 isetshenziswa, ngokwesibonelo, kumatheminali kuya ezintweni zokushisa, izakhi ze-porcupine zokushisisa umoya, nasezintweni zokushisisa isithando somlilo.
UKWAKHIWA KWAKHEMICAL
| C% | Si% | Mn% | Cr% | Al% | Fe% | |
| Ukuqamba igama | 5.3 | U-Bal. | ||||
| Okuncane | - | - | - | 23.0 | - | |
| Ubukhulu | 0.05 | 0.5 | 0.45 | 25.0 | - |
IZIMPAHLA ZEMITHETHO
| Ubukhulu | Amandla esivuno | Amandla aqinile | Ukwelula | Ukuqina |
| I-R0.2 | Rm | A | ||
| mm | Mpa | I-MPa | % | Hv |
| 2.0 | 450 | 650 | 18 | 200 |
IZIMPAHLA ZOMZIMBA
| Ukuminyana g/cm3 | 7.15 |
| Ukumelana nogesi ku-20°C Ω mm/m | 1.35 |
| Izinga lokushisa eliphezulu lokusebenzisa u-°C | 1300 |
| Iphuzu lokuncibilika °C | 1500 |
| Impahla Magnetic | Uzibuthe |
I-TEMPERATURE FACTOR OF REISTIVITY
| Izinga lokushisa °C | 200 | 300 | 400 | 500 | 600 | 700 | 800 | 900 | 1000 | 1100 | 1200 | 1300 |
| Ct | 1.00 | 1.01 | 1.01 | 1.02 | 1.03 | 1.03 | 1.04 | 1.04 | 1.04 | 1.05 | 1.05 | 1.05 |