I-OCr21AI4 (214),I-FCHW-2 I-FeCrAl Heating Wire yesithando somlilo
0Cr21Al4
Ulwazi oluvamile
I-FeCrAl, umndeni we-iron-chromium-aluminium alloys (i-Kanthal APM, A-1, D ne-AF njll.) esetshenziswa ezinhlobonhlobo eziningi zokumelana nezicelo zokushisa okuphezulu nazo zisetshenziswa ngendlela yezintambo zokumelana.
Igama:intambo yokushisisa
umbala: oxidized noma ocwebezelayo
Iphakheji: Ikhathoni noma ikesi lokhuni njengoba kudingekile
Isicelo: ukwenza izinto zokufudumeza ezifana nesithando somlilo sezimboni, into esetshenziswayo yokushisisa umphakathi, izihlungi ezihlukene zikagesi kanye ne-locomotive braking resistor.
Indawo Yomsuka: Jiangsu, China (Mainland)
Ukuqokwa | Izingxenye | |||||||
Ni | Fe | Zn | Mn | Cu | AI | Cr | Si | |
I-NCHW-1 | 77 min | 2.5 Max | 19-21 | 0.75~1.5 | ||||
I-NCHW-2 | 57 min | 1.5 ubuningi | 15-18 | 0.75~1.5 | ||||
I-FCHW-1 | i-rem | 1.0 Ubukhulu | 4.0~6.0 | 23-26 | 1.5 Min | |||
I-FCHW-2 | i-rem | 1.0 Ubukhulu | 2.0~4.0 | 17-22 | 1.5 Min |
Ukusetshenziswa: Resistor
Ubukhulu: Ubukhulu 0.01-7mm, ububanzi 1mm-1000mm
Ubuso: BA, 2B
I-alloy material | Ukwakheka kwamakhemikhali % | |||||||||
C | P | S | Mn | Si | Cr | Ni | Al | Fe | abanye | |
ubuningi(≤) | ||||||||||
I-Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.60 | 20.0-23.0 | Phumula | ≤0.50 | ≤1.0 | - |
I-Cr30Ni70 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.60 | 28.0-31.0 | Phumula | ≤0.50 | ≤1.0 | - |
I-Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.60 | 15.0-17.0 | 55.0- 61.0 | ≤0.50 | Phumula | - |
I-Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1 | 1.00-3.00 | 18.0-21.0 | 34.5-36.0 | - | Phumula | - |
I-Cr20Ni30 | 0.08 | 0.02 | 0.015 | 1 | 1.00-2.00 | 18.0-21.0 | 30.0-31.5 | - | Phumula | - |
1Cr13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | - | 3.5-4.5 | Phumula | - |
0Cr15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | - | 4.5-5.3 | Phumula | - |
0Cr25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | Phumula | - |
0Cr23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Phumula | - |
0Cr21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | Phumula | - |
1Cr20Al3 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 18.0-21.0 | ≤0.60 | 3.0-4.2 | Phumula | - |
0Cr21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | Phumula | Nb engeza0.5 |
0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.2 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | Phumula |
ngendlela yocingo, iribhoni kanye ne-strip
Intambo: 0.018mm-10mm
Iribhoni: 0.05*0.2mm-2.0*6.0mm
Uhlaka: 0.5 * 5.0mm-5.0 * 250mm
Ukupakisha Nokulethwa
Imininingwane yokupakisha: | ifilimu yepulasitiki ngaphakathi, ama-pallets okhuni ngaphandle, khetha ukupakisha okufanele, kungenziwa ngokwezifiso ngesidingo samakhasimende. |
---|---|
Imininingwane Yokulethwa: | cishe izinsuku ezingu-5-25 |
KUNGANI USIKHETHA?
Yonke impahla yethu eluhlaza yenziwe ngezinto eziphambili, hhayi izinto ezigaywe kabusha.Sinesipiliyoni seminyaka engaphezu kwe-10 ekukhiqizeni ukumelana nokushisa ama-alloys.
Emakethe, akuwona wonke ama-alloys e-NiCr anokwakheka kwamakhemikhali okujwayelekile nokumelana okuzinzile.Professional futhi enokwethenjelwa umphefumulo ibhizinisi lethu.
1) Sifinyelela ukukhiqizwa okungaguquki kusuka ekuncibilikeni kuya ekuqedeni imikhiqizo, siyakwazi ukuhlinzeka ngemikhiqizo egculisayo.
2) Sinezinga eliphezulu emhlabeni jikelele le-German ALD - VIDP1000 - 8000KG yesithando somlilo sokungeniswa kwe-vacuum kanye nemishini yokudweba ngocingo evela e-Japan.
3) Ngolwazi lwethu lwe-spooling olunekhono, sikhulise ngempumelelo isisindo sokuthatha i-spool.Isibonelo, ngisho nocingo oluhle kakhulu oluwububanzi obungu-0.04 mm lungalinyazwa futhi luthunyelwe nge-bobbin engu-3 - 4 kg, ngaleyo ndlela kube nomthelela ngokushesha ekusebenzeni kwakho kahle kokukhiqiza.
4) Ukuze kuvinjwe ucingo ukuthi lungaxegi, sethule amasistimu athuthukisiwe okulawula ukungezwani emshinini wethu wokuthatha kanye nomshini wokuhlanganisa kabusha.